C-UV 9400HT TECHNICAL DATA SHEET

PRODUCT DESCRIPTION 产品介绍

C-UV 9400HT is an ABS like SL resin which has accurate and durable features. It is designed for solid state SLA platforms. C-UV 9400HT can be applied in master patterns, concept models, general parts and functional prototypes in the field of automotive, medical and consumer electronics industries.The parts duability building with C-UV 9400HT is over 6.5months.C-UV 9400HT 是一种具备精确和耐久特性的类ABS的立体光造型树脂。它被用于固态激光的光固化成型法。C-UV 9400HT可应用于于汽车，医疗，消费电子等工业领域的母模，概念模型，一般部件，功能性部件的制作。用C-UV 9400HT树脂制造的部件的耐久性长达6.5个月以上。

TYPICAL FEATURES典型特点

-Liquid resin`s medium viscosity, so easy recoating, easy clean parts and machines 中等粘度的液态树脂，确保其更容易涂层以及清洗部件和机器

-Improved strength retained, improved dimensions retention of parts in humid condition 在潮湿环境中具有更好的强度及尺寸保持特性

-need minimal part finishing只需要极小的部件修饰

-Long shelf life in machine更长的实际使用期限

TYPICAL BENEFITS典型优点

-Need less part finishing time,easier post-curing 更少的部件完成时间

-Buliding accurate and high tough parts with an improved dimensional stability 能够建造精确和高韧性的部件并提高了部件的尺寸稳定性

-High quality controls for vacuum casting parts 对于真空铸造部件的高质量控制

-Low shrink and good resistance to yellowing 低收缩和优异的耐黄变性

-Magnificent white color 华丽的白色外观

-Outstanding machinable SLA material 卓越的可加工性

-Outstanding temperature resistant 卓越的耐温性能

Physical Properties – Liquid Material 液态材料的物理性能

Appearance外观	White白色
Density 密度	1.11-~1.15g/cm³ @ 25 ℃
Viscosity 粘度	405~500 cps @ 25 ℃
Dp 固化深度	0.135~0.152 mm
Ec 临界曝光量	8.9~9.5 mJ/cm²
Building layer thickness 建造层厚	0.05~0.12mm

Mechanical Properties of Post-Cured Material 固化后材料的机械性能

MEASUREMENT测试项目	TEST METHOD 测试方法	VALUE 数值
		90-minute UV post-cure 90分钟紫外固化
Hardness 硬度, Shore D	ASTM D 2240	77~88
Flexural modulus 弯曲模量, Mpa	ASTM D 790	2,682-2,778
Flexural strength 弯曲强度, Mpa	ASTM D 790	70- 74
Tensile modulus 拉伸模量, MPa	ASTM D 638	2,599-2,715
Tensile strength 拉伸强度, MPa	ASTM D 638	40-58
Elongation at break 断裂延长率	ASTM D 638	7 -12%
Poisson`s Ratio泊松比	ASTM D 638	0.4-0.44
Impact strength notched Izod, J/m 缺口冲击强度	ASTM D 256	30 - 37
Heat deflection temperature, ℃ 热变形温度	ASTM D 648 @66PSI	55~68
Glass transition,Tg 玻璃化转变温度，℃	DMA，E”peak	60~75
Coefficient of thermal expension,热膨胀系数, /℃	TMA(T	90~102*E-6
Density 密度, g/cm³		1.12~1.18
Dielectric Constant介电常数 60 Hz	ASTM D 150-98	4.1~5.0
Dielectric Constant介电常数 1 kHz	ASTM D 150-98	3.2~4.2
Dielectric Constant介电常数 1 MHz	ASTM D 150-98	3.2~4.1
Dielectric Strength绝缘强度 kV/mm	ASTM D 1549-97a	12.7~16.2