C-EP 1728是一种双组分环氧浇铸胶。该产品被设计用于需要抵抗高的机械冲击和热冲击场合。特别是用于灌封刚性或柔性的乙烯基电线引线。
固化前材料性能
Properties 性能 |
Test Method 测试方法 |
Resin-A 环氧树脂-A |
Hardener-B 固化剂-B |
Mixed-A/B 混合物-A/B |
Color/Appearance 颜色/外观 |
Visual 目测法 |
Paste like liquid, Black or natural 糊状黑色或自然色液体 |
Light colored liquid 浅色液态 |
Black or natural 黑色或自然色 |
Specific Gravity 比重 |
ASTM D-792 |
1.6 |
1.05 |
1.5 |
Viscosity @ 25°C, cps 粘度(25°C) |
ASTM D-2393 |
60,000-90,000 |
14 - 20 |
1800 - 2500 |
Shelf life, 25°C, month保质期,月 |
|
12 |
12 |
|
固化后属性
Property 性能 |
Test Method 测试方法 |
value 数值 |
Hardness (Shore D) 硬度 |
ASTM D-2240 |
82 |
Elongation at break 断裂延伸率,% |
|
3 |
Tensile strength 拉伸强度,psi |
|
8600 |
Compressive strength 抗压强度, psi |
|
22,000 |
Flexural strength, 弯曲强度psi |
ASTM D790 |
15,000 |
Impact strength, 冲击强度ft-lb/in |
|
0.5 |
Heat deflection temperature, 热变形温度 ºC at 264 psi |
|
90 |
Thermal Conductivity 导热率, W/M-K |
|
0.46 |
Coefficient of thermal expansion 热膨胀系数, CTE |
ASTM D3386 |
47 E-06 |
Water absorption吸水率,% weight,24 hours |
|
0.2 |
Volume resistivity 体积电阻率, ohms-cm |
|
4.0E14 |
Dielectric constant 介电常数 |
ASTM D150 |
4.5(100Hz), 4.4(10 Hz) |
Dissipation factor 耗散因子 |
|
0.009(100Hz), 0.016(10kHz) |
Arc resistance, seconds 弧抗,秒 |
|
140 |
Dielectrics strength, 介电强度, V/mil |
10mil thick |
1525 |
固化步骤
Resin/Hardener Ratio (by weight) 树脂与固化剂重量比 |
100 / 15 |
Resin/Hardener Ratio (by volume) 树脂与固化剂体积比 |
100 / 24 |
Pot Life (200 gram mass), 25°C, minutes 保质期(200g)25°C,分钟 |
70-90 |
固化进度表
Temperature 温度 |
Minimum Cure Time 最少固化时间 |
25 ºC (77ºF) |
24 hours 24小时 |
60 ºC (158ºF) |
3 hours 3小时 |
保存方法
每次用完后,应密封保存于15 - 30 ºC的干燥地方。