C-EP 9611 is a single component, solventless, heat curable, electrically conductive, modified epoxy adhesive. C-EP 9611是一款单组分改性环氧体系的热固化无溶剂导电胶。C-EP 9611具有以下优势:
Low stress 低应力
Good adhesion on nearly all surface 与绝大多数物质表面有很好的粘结性。
Mismatched TCE application 热膨胀系数失配的表面应用
Useful up to 200°C 使用温度可达200°C
PROPERTIES OF UNCURED MATERIAL 固化前材料性能
Properties 性能 |
Test Method测试方法 |
Resin-A环氧树脂 |
Color/Appearance 颜色/外观 |
TP-76W |
Silver银色 |
Specific Gravity比重, g/cm3比重 |
TP-13W |
3.10-3.14 |
Viscosity @ 25°C, cps 粘度(25°C) |
TP-11W |
120,000-140,000 |
TYPICAL CURED PROPERTIES 固化后属性
Cured 7 days @ 25 ºC (77ºF)(固化七天@25 ºC)
Property 性能 |
value 数值 |
Tensile lap shear strength,psi@ 25 ºC |
435 |
Thermal Conductivity 导热率, W/M-K |
4 |
Max. service temperature 最大工作温度, ºC |
200 |
Glass transition temperature玻璃化转变温度, ºC |
24 |
Volume resistivity 体积电阻率, ohms-cm |
0.001 |
CURING TIME TABLE 固化进度表
Temperature 温度 |
Minimum Cure Time 最少固化时间 |
110 ºC |
2 hours |
120 ºC |
1.5 hours |
150 ºC |
40 minutes |
175 ºC |
15 minutes |
SHELF LIFE储藏寿命
Provided this material is stored under the recommended storage conditions of -18 to -25ºC in their original containers, it will remain in useable condition for half year from date of shipping. 采用原始包装,保存于-18 to -25ºC的干燥地方,保质期为半年(从发货之日算起)。